Low Temperature Expandable Graphite
Product Detail
CAS No.: 7782-42-5
| Products No. |
Expansion Start Temperature (EST‚ °C) |
pH | Mesh |
Packing Density (mg/cm3) |
Expansion Volume (EV‚ ml/g) |
Property |
|
CXG00122 (EG-110-230) (Discontinued) |
110 | 7.0 | 80 | 0.6 | 230 |
Super-low Expansion Start Temperature |
|
EG-150-230 (Discontinued) |
150 | 7.0 | 80 | 0.6 | 230 |
Please also check our Expandable Graphite.
|
SKU |
Particle Size |
Purity (%) |
Expansion Start Temperature (EST‚ °C) |
Expansion Volume (EV‚ ml/g) |
Highlights and Application |
|
CXG22022 |
80%<75um |
≥92% |
190℃±10℃ |
≥20 ml/g |
Application: Coatings, Paints, Adhesive, and Textile, which requires finer particle size. |
|
CXG21122 |
80%<150 um |
≥94% |
180℃±10℃ |
≥35 ml/g |
Application: Coatings, Paints, Adhesive, and Textile, which requires finer particle size, in case CXG22022 cannot satisfy the flame retardance requirements. |
|
CXG21222 |
80%<150 um |
≥94% |
180℃±10℃ |
≥95 ml/g |
Application: Coatings, Paints, Adhesive, and Textile, which requires finer particle size, in case CXG21122 cannot satisfy the flame retardance requirements. |
|
CXG52322 |
80%>150 um |
≥95.0% |
180℃±10℃ |
≥200 ml/g |
Application: Spray foams, which require fine particle size. |
|
CXG8B122 |
80%>180 um |
≥95.0% |
180℃±10℃ |
≥230 ml/g |
Standard product with fine particle size. Application in PU foam, EPS foam, Sealing Strip, etc. |
|
CXG5B122 |
80%>300 um |
≥95.0% |
180℃±10℃ |
≥250 ml/g |
Standard product for all main applications, like PU foam, Coating, Rubber, Adhesive, Construction Materials, etc. |
|
CXG5B022 |
80%>300 um |
≥99.0% |
180℃±10℃ |
≥250 ml/g |
Same expansion, but higher purity than CXG5B122 |
|
CXG5C022 |
80%>300 um |
≥98.0% |
170℃±10℃ |
≥350 ml/g |
High purity, very high free expansion and expansion strength. Application: for all main applications which requires better flame-retardant effects than CXG5B122. |
| SKU |
Mesh |
Purity (%) |
Expansion Start Temperature (EST,°C) |
Expansion Volume (EV, ml/g) |
Highlights and Application |
| *CXGAA222 |
150 |
≥92% | 175℃ | ≥150 ml/g | Mainly used in fabric coatings, fire-resistant adhesives and EPS and XPS flame retardants |
| *CXG00522 |
80 |
≥95% | 250℃ | ≥180 ml/g |
With application where extruder used |
| *CXG00622 |
50 |
≥95% | 300℃ | ≥170 ml/g | Highest Expansion Start Temperature |
*These three products will be discontinued after sold out.
Disclaimer: ACS Material LLC believes that the information on our website is accurate and represents the best and most current information available to us. ACS Material makes no representations or warranties either express or implied, regarding the suitability of the material for any purpose or the accuracy of the information listed here. Accordingly, ACS Material will not be responsible for damages resulting from use of or reliance upon this information.
Research Citations of ACS Material Products
- Meduri, Kavita. "Carbon-Supported Transition Metal Nanoparticles for Catalytic and Electromagnetic Applications." (2018).
- Meduri, Kavita, Candice Stauffer, Wen Qian, Otto Zietz, Andrew Barnum, Graham O’Brien Johnson, Dimin Fan et al. "Palladium and gold nanoparticles on carbon supports as highly efficient catalysts for effective removal of trichloroethylene." Journal of Materials Research 33, no. 16 (2018): 2404-2413.