Polyurethane Thermal Conductive Structural Adhesive
Product Detail
The Polyurethane Thermal Conductive Structural is a dual-component polyurethane thermal conductive structural adhesive with a thermal conductivity available in 1.2 W/m-K and 2.0 W/m-K. It is suitable for bonding between battery cells and cooling plates; and can be utilized for automated adhesive assembly. This material is mixed thoroughly by A and B components through a helical mixing tube. It can cure at room temperature as well at high temperatures. The adhesive surface stress is extremely low (virtually absent), ensuring excellent adhesion to the material interface and resulting in low thermal resistance. Once cured, it securely bonds the battery cells to the cooling plate. Its exceptional structural performance and weather resistance make it particularly suitable for adhesive applications in new energy vehicles. Moreover, the thermal conductive structural adhesive adopts a polyurethane formulation system. It is non-toxic, odorless, non-corrosive, and complies with RoHS directives and relevant environmental requirements.
1. Features
- Good insulation and high/low temperature resistance.
- Flame retardant rating of UL94 V0
- Good maneuverability and flexibility
2. Characterizations
|
Before Curing |
|||||
|
Type |
A |
B |
Testing Standard |
||
|
|
Tube 1 |
Tube 2 |
Tube 1 |
Tube 2 |
- |
|
Color |
Off-White |
Black |
Red/Optional (color can be changed) |
White |
- |
|
Viscosity @25℃ 7#rotor 5rpm |
1.0x10^5 cps - 3.0x10^5 cps
|
1.0x10^5 cps - 3.0x10^5 cps | 2.0x10^5 cps | 2.3x10^5 cps |
ASTM D445 |
|
Density |
1.75 g/cc |
1.82 g/cc |
2.0 g/cc |
2.0 g/cc |
ASTM D792 |
|
Mixing Ratio |
1 |
1 |
1 |
1 |
- |
|
After Curing |
|||||
|
Thermal Conductive |
1.2 W/m*K |
2.0 W/m*K |
IS022007-2 |
||
|
Density |
1.8 g/cc |
2.0 g/cc |
ASTM D792 |
||
|
Hardness |
≥60 Shore00 |
70 Shore00 |
ASTM D2240 |
||
|
Flame Retardant Rating |
V0 |
V0 |
UL94 |
||
|
Surface Dry Time @23℃ |
60-90 min |
20 min |
Manual |
||
|
Curing Time @ 25℃ |
7 D |
7 D |
Hardness Test |
||
|
Tensile Strength |
10.0 MPa |
8.0 MPa |
GB/T528 | ASTM D412 |
||
|
Aluminum-Aluminum Bond Shear Strength |
9.0MPa |
8.0 MPa |
GB/T 7124 | ASTM D412 |
||
|
Shear Strength (untreated, PET/ET Film) |
2.0 MPa |
5.0 MPa |
GB/T 7124 | ASTM D412 |
||
|
Elongation at Break |
5% |
5% |
ISO 10563 | ASTM D149 |
||
|
Breakdown Voltage |
12 kV/mm |
12 kV/mm |
ASTM D149 | ASTM D257 |
||
|
Volume Resistivity |
>1012 Ohm*cm |
>1012 Ohm*cm |
ASTM D257 | GC |
||
|
Recommended using temperature range |
-40 ~ 80℃ |
-40 ~ 80℃ |
- |
||
3. Storage Conditions
Shelf life: 6 months
Storage conditions: Temperature: 15°C < T < 30°C
Relative humidity: RH<70%
Disclaimer: ACS Material, LLC believes that the information in this Technical Data Sheet is accurate and represents the best and most current information available to us. ACS Material makes no representations or warranties either express or implied, regarding the suitability of the material for any purpose or the accuracy of the information contained within this document. Accordingly, ACS Material will not be responsible for damages resulting from use of or reliance upon this information.